["stamsund" <stamsund@xxxxxxxxxxxxxx>]

Neal,

You heat it then quench it with water to soften it.

Rob

----- Original Message ----- 
From: "Neal Namowicz" <neal@xxxxxxxxxxxxxxxx>
To: "Tesla Coil Mailing List" <tesla@xxxxxxxxxx>
Sent: Friday, July 11, 2008 10:37 AM
Subject: Re: [TCML] Winding the primary


> I have a couple of lengths of  "salvaged" tubing myself with a few too many 
> bends in it. I wouldn't have bothered in the past, but with the cost of 
> copper... Anyway, I was wondering if anyone has managed to UN-work harden 
> tubing? I was thinking of sticking it in the oven on high heat for a while 
> and letting it slowly cool. Anyone ever try it? It's a pain in the neck, 
> sure, but compared to unpotting an nst for example, it doesn't sound too 
> bad.
>
> Neal.
>
>
> ----- Original Message ----- 
> From: "Quarkster" <quarkster@xxxxxxx>
> To: "Tesla Coil Mailing List" <tesla@xxxxxxxxxx>
> Sent: Tuesday, July 08, 2008 11:18 PM
> Subject: Re: [TCML] Winding the primary
>
>
> > Steve -
> >
> >  What is your primary conductor? If you're using copper tubing, here are 
> > a few tips:
> >
> >  1. Use virgin refrigeration tubing, and leave it in the coiled shape 
> > that it comes in. Don't try to re-use "salvaged" tubing if you want a 
> > nice looking primary. Copper tubing "work-hardens" and stiffens very 
> > rapidly as you deform it, so deform it as little as possible.
> >
> >  2. DO NOT try to straighten the tubing, then re-form it into a spiral. 
> > The tubing will work-harden, then is likely to kink and become 
> > unmanagable.
> >
> >  3. Have an assistant hold the coil of tubing about a foot above your 
> > primary forms, and just let one coil drop down at a time. The typical 
> > diameter of a coil of rerfigeration tubing is around 18", so I start at 
> > the end of the primary that is closest in diameter to the diameter of the 
> > coil of tubing. For a small diameter primary this means starting at the 
> > OUTSIDE of the primary form and wind inward. For a large diameter 
> > primary, this means starting at the INSIDE of the primary form and 
> > winding outward. This way the tubing requires minimum deformation 
> > initially, and then must be gradually formed into a larger or smaller 
> > radius as you move outward or inward.
> >
> >  Regards,
> >  Herr Zappp
>
> _______________________________________________
> Tesla mailing list
> Tesla@xxxxxxxxxxxxxx
> http://www.pupman.com/mailman/listinfo/tesla