[Home][2016 Index] Re: [TCML] Spark Gap Electrodes - Flat or Rounded [Date Prev][Date Next][Thread Prev][Thread Next][Date Index][Thread Index]

Re: [TCML] Spark Gap Electrodes - Flat or Rounded



Okay Phil, I will use 80%W, 20%Cu. Maybe this makes the difference ;-) However, I will give it a try...


----- Original Message ----- From: "Phil" <pip@xxxxxxxxxxx>
To: "'Tesla Coil Mailing List'" <tesla@xxxxxxxxxx>
Sent: Wednesday, January 20, 2016 10:44 PM
Subject: Re: [TCML] Spark Gap Electrodes - Flat or Rounded


Update:  Stuff I used Stephan is apparently 70%W, 30%Cu.

Phil


-----Original Message-----
From: Tesla [mailto:tesla-bounces@xxxxxxxxxx] On Behalf Of Phil
Sent: 20 January 2016 20:15
To: 'Tesla Coil Mailing List'
Subject: Re: [TCML] Spark Gap Electrodes - Flat or Rounded

You could use a bench grinder, but you would end up putting a groove in the wheel as they (wheels) don't have much width. Also wheels are dearer than belt sander / Linisher belts. If they are Thoriated DON'T breathe the dust, for others it's best avoid breathing the dust, (especially so if like me you have asthma, - I found that after grinding without a mask a few years back)

Phil

-----Original Message-----
From: Tesla [mailto:tesla-bounces@xxxxxxxxxx] On Behalf Of wt5y
Sent: 20 January 2016 16:16
To: Tesla Coil Mailing List
Subject: Re: [TCML] Spark Gap Electrodes - Flat or Rounded



What a bench grinder? Or would that tame too much too fast? Are there breathing hazards from dust


Sent from my Samsung GALAXY S5™, a Cricket 4G LTE smartphone

-------- Original message --------
From: Phil <pip@xxxxxxxxxxx>
Date: 01/20/2016  05:55  (GMT-06:00)
To: 'Tesla Coil Mailing List' <tesla@xxxxxxxxxx>
Subject: Re: [TCML] Spark Gap Electrodes - Flat or Rounded

Matthew,
You can round out the ends of Tungsten (in my case 0.25") by a belt sander or linisher, and using a drill. It WILL wreck the belt though, but I find I can do eight ends on an already used belt ok. Start the belt and chuck the Tungsten in the drill and simply hold against revolving belt. I used to make half hemispheres but now I find just rounding the edges is sufficient - just need to lose the 90 degree edge.

You can just make the curve out in third photo down:
http://www.hvtesla.com/srsg_2015.html (statics are 3/8 Tung / Copper, revolving are pure Tungsten)

Green welding rods (pure) are harder to do than those that are doped with something, I have found though.

Tungsten copper will cut very easily and you can round those with a file, but it ablates quicker (3/8 inch Diam' on 7kw or so)


Phil




_______________________________________________
Tesla mailing list
Tesla@xxxxxxxxxx
http://www.pupman.com/mailman/listinfo/tesla


_______________________________________________
Tesla mailing list
Tesla@xxxxxxxxxx
http://www.pupman.com/mailman/listinfo/tesla